| Description |
| “FLORES” Aluminum composite panel is consisted of 3 layers, the surface and back covers of high strength aluminum alloy sheets and the core of nontoxic low density polyethylene (PE) sheet. The painting in the surface and back aluminum sheets are from PPG.VALSPAR of USA and Becker of Sweden. Strictly according to the international quality system ISO9001 and ISO14001 produce superior quality PE aluminum composite panels. Our PE aluminum composite panels not only passed GB/T1778-1999, they are also passed SGS tests and gained CE certificate. |
|
|
| Specifications: |
Thickness: 3mm-6mm
Thickness of aluminum sheets: 0.12mm, 0.15mm,0.18mm, 0.2mm, 0.3mm, 0.4mm, 0.45mm,0.5mm
Width: 1,220, 1,250, 1,270, 1,500, 1,550 and 1,575mm
Length: standard 2,440mm and customized length ≤ 6,000mm
Standard size: 1,220 x 2,440mm (Nonstandard sizes available according to your requirements
Colors: Refer to color chart, or RAL colors
Core: PE or fire-proofing
Coating: PE
| |
| Applications: |
※Applications:Constructional exterior curtain walls;
※Decorative renovation for storey-added old buildings;
※ Indoors decoration for interior walls, ceilings, bathrooms, kitchens and balconies;
※ Advertisement board, display platforms and signboards;
※Wallboard and ceilings for tunnels;
※ Raw materials in industrial purpose;
※Materials used for vehicle and boat.
|
| Test report for 3mm polyester ACP |
|
Items |
Standard index of quality product |
Result |
Conclusion |
|
Appearance |
Clean surface without swell,flaws.scrath and aberration |
pass |
Qualified |
|
|
aberration |
|
Qualified |
|
|
Length: ± 3mm |
0mm~+1mm |
Qualified |
|
|
Width: ± 2mm |
0mm~+1mm |
Qualified |
|
|
Thickness: ±0. 2mm |
0mm~+0.14mm |
Qualified |
|
Deviation of dimension |
Deviation of diagonal: ≤ 5mm |
0mm |
Qualified |
|
|
Out of straight at sides: ≤ 1mm/m |
0.2mm/m |
Qualified |
|
|
Warp: ≤ 5mm/m |
1mm/m |
Qualified |
|
Thickness of coating |
≥ 16um |
17um （av.18 ） |
Qualified |
|
Deviation of luster |
≤ 10 |
2.6 （ av.20 ） |
Qualified |
|
Hardness of pencil |
≥ HB |
2H |
Qualified |
|
Toughness of coating |
≤ 3T |
1T |
Qualified |
|
Adhesive |
Not less than Grade1 |
Squaring off method of Grade 0 Grade 1marking method of rolling line |
Qualified |
|
Impact strength |
50Kg.cm Without paint off and crack |
Pass |
Qualified |
|
Boiling water resistance |
(Boiling for 2h without change) |
Unchanged |
Qualified |
|
Acid resistance |
Immerse surface with2%HCI(v/v)for 24H without change |
Unchanged |
Qualified |
|
Oil resistance |
Immerse surface with 20# engine oil for 24h without change |
Unchanged |
Qualified |
|
Solvent resistance |
Clean 100 times with dimethylbenzene without change |
Bottom unrevealed |
Qualified |
|
Cleaning resistance |
≥ 10000 （ ≥ 10000 times without change） |
Unchanged |
Qualified |
|
Abrasion resistance Density of surface |
Specified value: ± 0.5Kg/m 2 |
3.63Kg/m 2 |
Qualified |
|
Bend strength |
≥ 60Mpa |
79.6Mpa |
Qualified |
|
Flexuous modulus of elasticity |
≥ 1.5×10 4 Mpa
|
2.19 × 10 4 Mpa |
Qualified |
|
Through resistance |
≥ 5.0kN |
6.25kN |
Qualified |
|
Cutting strenght |
≥ 20.0Mpa |
25.7Mpa |
Qualified |
|
180 o peel strength |
≥ 5.0N/mm |
6.2N/mm |
Qualified |
|
Resistance to change of temperature |
-40 o C~80 o C 20 cycles without change |
Unchanged
|
Qualified |
|
Heat deformation temperature |
≥ 95oC |
116 o C |
Qualified |
|
Coefficient of heat expansion |
≤ 4.00×10 -5 oC -1 |
2.47 × 10 -5 o C -1 |
Qualified | |
| The test result meets the index requirements of quality product of GB/T17748-1999. |